Preparação por sol-gel de filmes granulados de CoCr2O4

Neste trabalho foi feito um estudo das propriedades estruturais e magnéticas de filmes granulares de cromita de cobalto sobre substrato de silicio. Aqui os filmes foram fabricados a partir do método químico sol‐gel, técnica de centrifugação spincoating e Tratamento térmico apropriado. Toda família...

Full description

Main Author: FARIAS, Bruno Veríssimo de Miranda
Other Authors: HERNANDEZ, Eduardo Padrón
Format: masterThesis
Language: por
Published: Universidade Federal de Pernambuco 2017
Subjects:
Sol-­‐gel. Filmes granulares. Spin coating.
Sol-­‐gel. Granular film. Spin coating.
Online Access: https://repositorio.ufpe.br/handle/123456789/20045
Tags: Add Tag
No Tags, Be the first to tag this record!
id ir-123456789-20045
recordtype dspace
spelling ir-123456789-200452019-10-26T00:43:46Z Preparação por sol-gel de filmes granulados de CoCr2O4 FARIAS, Bruno Veríssimo de Miranda HERNANDEZ, Eduardo Padrón http://lattes.cnpq.br/7175167116300720 http://lattes.cnpq.br/3590036930228473 Sol-­‐gel. Filmes granulares. Spin coating. Sol-­‐gel. Granular film. Spin coating. Neste trabalho foi feito um estudo das propriedades estruturais e magnéticas de filmes granulares de cromita de cobalto sobre substrato de silicio. Aqui os filmes foram fabricados a partir do método químico sol‐gel, técnica de centrifugação spincoating e Tratamento térmico apropriado. Toda família de filmes foi fabricada sobre substrato de silício (100) e submetida a tratamento termico. A diferença de um filme para outro esta na quantidade de material depositado. Isto possibilitou o estudo das propriedades supracitadas em função da quantidade de material depositado para fabricação do filme. A cristalinidade de todas as amostras obtidas foi confirmada por difração de raios-X (XRD). A microscopia eletrônica de varredura (MEV) mostrou filmes granulares com boa homogeneidade e que a espessura de todas as amostras aumenta com a quantidade de gotas depositadas durante o spin‐coating. As propriedades magnéticas foram medidas usando magnetometria de amostra vibrante (VSM). O campo aplicado durante a medicao foi orientado paralelo ao plano do filme e observou‐se uma alta coercividade e que esta diminui quase linearmente com o aumento de temperatura. In this work we have made a study of the structural and magnetic properties of cobalt chromite granular films over silicon substrate. Here the films were fabricated by the chemical method sol‐gel, spin coating technique and ppropriate heat treatment. The entire Family was deposited over silicon substrate (100) and submitted to heat treatment. The difference between a film to another is the quantity of deposited Material. This allowed the study of the above properties as a function of the deposited material. The crystallinity of all samples obtained was confirmed by X‐ray diffraction (XRD). The scanning electron microscopy (SEM) showed granular films with good homogeneity and the thickness of all samples increases when the number of drops increases during spin‐coating. The magnetic properties were measured using vibrating sample magnetometry (VSM). The applied field during the measurement was Oriented parallel to the film plane and observed a high coercivity and that decreases pproximately linearly with increasing temperature. 2017-07-25T19:46:06Z 2017-07-25T19:46:06Z 2015-07-02 masterThesis https://repositorio.ufpe.br/handle/123456789/20045 por Attribution-NonCommercial-NoDerivs 3.0 Brazil http://creativecommons.org/licenses/by-nc-nd/3.0/br/ application/pdf Universidade Federal de Pernambuco UFPE Brasil Programa de Pos Graduacao em Ciencia de Materiais
institution REPOSITORIO UFPE
collection REPOSITORIO UFPE
language por
topic Sol-­‐gel. Filmes granulares. Spin coating.
Sol-­‐gel. Granular film. Spin coating.
spellingShingle Sol-­‐gel. Filmes granulares. Spin coating.
Sol-­‐gel. Granular film. Spin coating.
FARIAS, Bruno Veríssimo de Miranda
Preparação por sol-gel de filmes granulados de CoCr2O4
description Neste trabalho foi feito um estudo das propriedades estruturais e magnéticas de filmes granulares de cromita de cobalto sobre substrato de silicio. Aqui os filmes foram fabricados a partir do método químico sol‐gel, técnica de centrifugação spincoating e Tratamento térmico apropriado. Toda família de filmes foi fabricada sobre substrato de silício (100) e submetida a tratamento termico. A diferença de um filme para outro esta na quantidade de material depositado. Isto possibilitou o estudo das propriedades supracitadas em função da quantidade de material depositado para fabricação do filme. A cristalinidade de todas as amostras obtidas foi confirmada por difração de raios-X (XRD). A microscopia eletrônica de varredura (MEV) mostrou filmes granulares com boa homogeneidade e que a espessura de todas as amostras aumenta com a quantidade de gotas depositadas durante o spin‐coating. As propriedades magnéticas foram medidas usando magnetometria de amostra vibrante (VSM). O campo aplicado durante a medicao foi orientado paralelo ao plano do filme e observou‐se uma alta coercividade e que esta diminui quase linearmente com o aumento de temperatura.
author2 HERNANDEZ, Eduardo Padrón
format masterThesis
author FARIAS, Bruno Veríssimo de Miranda
author_sort FARIAS, Bruno Veríssimo de Miranda
title Preparação por sol-gel de filmes granulados de CoCr2O4
title_short Preparação por sol-gel de filmes granulados de CoCr2O4
title_full Preparação por sol-gel de filmes granulados de CoCr2O4
title_fullStr Preparação por sol-gel de filmes granulados de CoCr2O4
title_full_unstemmed Preparação por sol-gel de filmes granulados de CoCr2O4
title_sort preparação por sol-gel de filmes granulados de cocr2o4
publisher Universidade Federal de Pernambuco
publishDate 2017
url https://repositorio.ufpe.br/handle/123456789/20045
_version_ 1648655234165112832
score 13.657419

Similar Items